Modelling the deformation and fracture of an Al2O3 scale developed Fe3Al during cooling

Griffin, D., Daadbin, Ali and Datta, Psantu (2004) Modelling the deformation and fracture of an Al2O3 scale developed Fe3Al during cooling. Materials Science Forum, 461-46 (II). pp. 721-728. ISSN 0255 5476

Full text not available from this repository. (Request a copy)

Abstract

The deformation and fracture of oxide scales developed on Fe3Al, during cooling, has been modelled using finite element analysis FEA. Embedded defects have been introduced at the oxide surface and at the oxide/substrate interface and the propagation of these defects and the influence of such propagation on scale spallation has been analysed under both elastic and elastic plastic conditions. Relaxation of stresses associated with the plastic deformation of the substrate has been found to delay scale spallation and a greater temperature drop is required to cause spallation. In this situation, the presence of an oxide surface crack influences scale spallation in a complex manner. The oxide surface crack does not influence the scale spallation process for a purely linear elastic analysis, which is solely controlled by interfacial defects.

Item Type: Article
Uncontrolled Keywords: Finite element analysis, scale fracture, spallation
Subjects: F200 Materials Science
Department: Faculties > Engineering and Environment > Mechanical and Construction Engineering
Depositing User: Becky Skoyles
Date Deposited: 16 Jan 2015 12:31
Last Modified: 10 Aug 2015 11:37
URI: http://nrl.northumbria.ac.uk/id/eprint/21045

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics


Policies: NRL Policies | NRL University Deposit Policy | NRL Deposit Licence