Influence of indenter shape on DLC film failure during multiple load cycle nanoindentation

Faisal, Nadimul, Ahmed, Rashid, Fu, Yong Qing, Elakwah, Youssef and Alhoshan, Mansour (2012) Influence of indenter shape on DLC film failure during multiple load cycle nanoindentation. Materials Science and Technology, 28 (9-10). pp. 1186-1197. ISSN 0267-0836

Full text not available from this repository. (Request a copy)
Official URL: http://dx.doi.org/10.1179/1743284712Y.0000000039

Abstract

The aim of the present investigation is to understand the localised failure mechanism of diamond-like carbon (DLC) film during multiple load cycle nanoindentation. The DLC film investigated was 500 nm thick sputter coated on Si (100) wafer of 500 μm thickness. Multiple load cycle nanoindentation tests under diamond Berkovich and conical indenters were performed using a calibrated NanoTest at five different load ranges between 0·1 and 500 mN. Test results indicated forward deviation, no deviation and backward deviation of the force–displacement profile, which provided some insights to the mechanisms of localised film failure. During backward deviation, film failure starts from interfacial delamination. This was observed for a conical indenter in a particular load range (1–10 mN). An elastic finite element model during nanoindentation loading indicated that this was caused by the location of maximum stress near the interface. Forward depth deviation was observed for conical and Berkovich indenter at all the other load ranges.

Item Type: Article
Uncontrolled Keywords: Diamond-like carbon, multiple load cycle, nanoindentation, residual stress, film failure, finite element modelling, tribology
Subjects: F200 Materials Science
Department: Faculties > Engineering and Environment > Physics and Electrical Engineering
Depositing User: Becky Skoyles
Date Deposited: 23 Mar 2015 11:31
Last Modified: 24 Feb 2016 11:24
URI: http://nrl.northumbria.ac.uk/id/eprint/21693

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics


Policies: NRL Policies | NRL University Deposit Policy | NRL Deposit Licence