Electrode loading effect and high temperature performance of ZnO thin film ultrasonic transducers

Zhou, X. S., Zhang, Jia, Hou, Ruozhou, Zhao, Chao, Kirk, Katherine, Hutson, David, Hu, Ping An, Peng, Shuming, Zu, Xiao-Tao and Fu, Yong Qing (2014) Electrode loading effect and high temperature performance of ZnO thin film ultrasonic transducers. Applied Surface Science, 315. pp. 307-313. ISSN 0169 4332

Full text not available from this repository. (Request a copy)
Official URL: http://dx.doi.org/10.1016/j.apsusc.2014.07.114

Abstract

Nanocrystalline ZnO films of 5.8 μm thick were sputter-deposited on ferritic carbon steel plates (25 × 25 × 3 mm3) and characterized for use as ultrasonic transducers at both room temperature and high temperatures. Electrode loading effects have been studied using two types of electrodes, i.e., sputtered Cr/Au (5/50 nm) and silver paste, with electrode diameters 0.7–2.5 mm. Longitudinal and transverse waves were obtained in pulse-echo tests using both types of electrodes. With a silver paste top electrode, a dominant longitudinal mode was obtained, but with a thin Cr/Au film as the top electrode, shear waves were more dominant. Pulse-echo tests of the ZnO transducers were also performed at elevated temperatures up to 450 °C using a carbon paste electrodes. The sputtered ZnO films maintained a stable crystalline structure and orientation at the elevated temperatures, and ZnO devices on ferritic carbon steel could be used successfully up to 400 °C. However, when the temperature was increased further, rapid surface oxidation of the ferritic carbon steel caused the failure of the transducer.

Item Type: Article
Uncontrolled Keywords: ZnO film, ultrasonic transducer, electrode loading effect, high-temperature performance, ultrasonic wave
Subjects: F200 Materials Science
Department: Faculties > Engineering and Environment > Physics and Electrical Engineering
Depositing User: Becky Skoyles
Date Deposited: 23 Mar 2015 14:50
Last Modified: 31 Mar 2016 13:42
URI: http://nrl.northumbria.ac.uk/id/eprint/21732

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics


Policies: NRL Policies | NRL University Deposit Policy | NRL Deposit Licence