Electrical properties of TaN–Cu nanocomposite thin films

Wang, Chien Ming, Hsieh, Jang-Hsing, Fu, Yong Qing, Li, C., Chen, Tu Pei and Lam, U. T. (2004) Electrical properties of TaN–Cu nanocomposite thin films. Ceramics International, 30 (7). pp. 1879-1883. ISSN 0272 8842

Full text not available from this repository. (Request a copy)
Official URL: http://dx.doi.org/10.1016/j.ceramint.2003.12.051

Abstract

TaN–Cu nanocomposite thin films used as materials for TFR (thin film resistor) were prepared by reactive co-sputtering of Ta and Cu in the plasma of N2 and Ar. After deposition, the films were annealed using rapid thermal processing (RTP) at 400 °C for 2, 4, 8 min, respectively to induce the nucleation and grain growth of Cu. The results reveal that temperature coefficient of resistivity (TCR) values will increase with the increase of Cu content for both the as-deposited and annealed films. The increase of nitrogen will result in higher resistivity and more negative TCR. At a constant nitrogen flow rate, the resistivity and TCR may increase or decrease with the increase of annealing time depending on the Cu content. In general, to reach near-zero TCR value, more copper is needed to compensate the negative effect caused by Ta–N. Thus, electrical properties of thin films can be characterized as functions of N2 flow rate, Cu concentration and annealing time.

Item Type: Article
Uncontrolled Keywords: Nanocomposites; Resistivity; Thermal coefficient of resistivity; TaN–Cu; Thin film resistor
Subjects: F200 Materials Science
Department: Faculties > Engineering and Environment > Mathematics, Physics and Electrical Engineering
Depositing User: Becky Skoyles
Date Deposited: 26 Mar 2015 15:19
Last Modified: 24 Oct 2017 08:55
URI: http://nrl.northumbria.ac.uk/id/eprint/21832

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics


Policies: NRL Policies | NRL University Deposit Policy | NRL Deposit Licence