Improvement to thin film CdTe solar cells with controlled back surface oxidation

Rugen-Hankey, Sarah, Clayton, Andrew, Barrioz, Vincent, Kartopu, Giray, Irvine, Stuart, McGettrick, James and Hammond, Debbie (2015) Improvement to thin film CdTe solar cells with controlled back surface oxidation. Solar Energy Materials and Solar Cells, 136. pp. 213-217. ISSN 0927-0248

Full text not available from this repository. (Request a copy)
Official URL: http://dx.doi.org/10.1016/j.solmat.2014.10.044

Abstract

Thin film CdTe solar cells were produced by MOCVD, at atmospheric pressure, under a hydrogen atmosphere (i.e. oxygen-free). Window layer alloying with zinc (forming Cd1−xZnxS) and extrinsic p-type doping with arsenic (giving CdTe:As) have been used to improve photovoltaic solar cell performances, but as-grown MOCVD-CdTe PV cells are still typically characterised by low Voc (~620–690 mV). Post-deposition annealing in air for 30 min at low temperature (170 °C) prior to evaporation of the back contacts led to significant increases in Voc and FF. XPS measurements revealed back surface oxidation, resulting in formation of Te–O species. This was also the case for a device aged under ambient laboratory conditions. Extended annealing in air of a fresh device, for up to 180 min, continued to improve both Voc and FF. At longer annealing times the Voc remained relatively stable whilst the FF started to deteriorate. External quantum efficiency showed loss of photocurrent generation after excessive oxidation prior to back contact metallisation. Controlled back surface oxidation resulted in Voc values exceeding 800 mV and a best cell efficiency of 15.3%.

Item Type: Article
Uncontrolled Keywords: CdTe; Thin film; Photovoltaics; Open-circuit voltage; MOCVD
Subjects: F200 Materials Science
Department: Faculties > Engineering and Environment > Mathematics, Physics and Electrical Engineering
Depositing User: Becky Skoyles
Date Deposited: 23 Nov 2015 11:54
Last Modified: 24 Oct 2017 08:52
URI: http://nrl.northumbria.ac.uk/id/eprint/24668

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics


Policies: NRL Policies | NRL University Deposit Policy | NRL Deposit Licence