Tuning the Mechanical and Antimicrobial Performance of a Cu-Based Metallic Glass Composite through Cooling Rate Control and Annealing

Villapún, Victor, Esat, Faye, Bull, Steve, Dover, Lynn and Gonzalez Sanchez, Sergio (2017) Tuning the Mechanical and Antimicrobial Performance of a Cu-Based Metallic Glass Composite through Cooling Rate Control and Annealing. Materials, 10 (5). p. 506. ISSN 1996-1944

[img]
Preview
Text (Article)
materials-10-00506-v2 (1).pdf - Published Version
Available under License Creative Commons Attribution 4.0.

Download (3MB) | Preview
Official URL: https://doi.org/10.3390/ma10050506

Abstract

The influence of cooling rate on the wear and antimicrobial performance of a Cu52Z41Al7 (at. %) bulk metallic glass (BMG) composite was studied and the results compared to those of the annealed sample (850 °C for 48 h) and to pure copper. The aim of this basic research is to explore the potential use of the material in preventing the spread of infections. The cooling rate is controlled by changing the mould diameter (2 mm and 3 mm) upon suction casting and controlling the mould temperature (chiller on and off). For the highest cooling rate conditions CuZr is formed but CuZr2 starts to crystallise as the cooling rate decreases, resulting in an increase in the wear resistance and brittleness, as measured by scratch tests. A decrease in the cooling rate also increases the antimicrobial performance, as shown by different methodologies (European, American and Japanese standards). Annealing leads to the formation of new intermetallic phases (Cu10Zr7 and Cu2ZrAl) resulting in maximum scratch hardness and antimicrobial performance. However, the annealed sample corrodes during the antimicrobial tests (within 1 h of contact with broth). The antibacterial activity of copper was proved to be higher than that of any of the other materials tested but it exhibits very poor wear properties. Cu-rich BMG composites with optimised microstructure would be preferable for some applications where the durability requirements are higher than the antimicrobial needs.

Item Type: Article
Subjects: F200 Materials Science
Department: Faculties > Health and Life Sciences > Applied Sciences
Faculties > Engineering and Environment > Mechanical and Construction Engineering
Depositing User: Ay Okpokam
Date Deposited: 30 May 2017 14:53
Last Modified: 24 Oct 2017 11:23
URI: http://nrl.northumbria.ac.uk/id/eprint/30922

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics


Policies: NRL Policies | NRL University Deposit Policy | NRL Deposit Licence