Interfacial bonding mechanism and annealing effect on Cu-Al joint produced by solid-liquid compound casting

Li, Hanyan, Chen, Wenge, Dong, Longlong, Shi, Yingge, Liu, Jie and Fu, Yong Qing (2018) Interfacial bonding mechanism and annealing effect on Cu-Al joint produced by solid-liquid compound casting. Journal of Materials Processing Technology, 252. pp. 795-803. ISSN 0924-0136

[img] Text (Article)
J Mater Proc Technol-final version.pdf - Accepted Version
Restricted to Repository staff only until 31 October 2019.

Download (1MB)
Official URL: https://doi.org/10.1016/j.jmatprotec.2017.10.050

Abstract

Copper-aluminum (Cu-Al) based lamellar composites were prepared using a solid-liquid compound casting (SLCC) technology. Characterization results showed that the Cu-Al composites were fully-sintered at 700 °C under an argon atmosphere using the SLCC technology. Cu-Al interfacial bonding was uniform with a well-defined transitional and inter-diffusion region. Intermetallic compounds and solid solutions of CuAl2, CuAl, Cu9Al4, CuAl3 and Cu3Al2 were detected at the interfacial region. With the increase of annealing temperature, the width of the Cu-Al interfacial region was increased, and the interfacial bonding strength was also increased, whereas the types of the intermediate phases were changed. With the increase of dwelling time at a given annealing temperature, the width of Cu-Al interfacial region was increased, the interfacial bonding strength was decreased and the mesophases were changed. The bonding strength of the as-prepared composite was 30 MPa, whereas those of specimens annealed at 200 °C for 2 h, 300 °C for 2 h, 400 °C for 2 h, 300 °C for 30 min and 300 °C for 1 h were 59, 39, 74, 56, and 49 MPa, respectively. The Cu-Al interfacial bonding mechanisms were identified to be rapid inter-diffusion of copper and aluminum and formation of interfacial and graded microstructures. The formation of copper-aluminum interface is a combined result of inter-atomic diffusion and interfacial chemical reactions, the latter of which is more dominant in the diffusion process.

Item Type: Article
Subjects: F200 Materials Science
Department: Faculties > Engineering and Environment > Mathematics, Physics and Electrical Engineering
Depositing User: Ay Okpokam
Date Deposited: 07 Nov 2017 10:15
Last Modified: 07 Nov 2017 11:15
URI: http://nrl.northumbria.ac.uk/id/eprint/32465

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics


Policies: NRL Policies | NRL University Deposit Policy | NRL Deposit Licence