Annealing temperature effects on photoelectrochemical performance of bismuth vanadate thin film photoelectrodes

Shi, Le, Zhuo, Sifei, Abulikemu, Mutalifu, Mettela, Gangaiah, Palaniselvam, Thangavelu, Rasul, Shahid, Tang, Bo, Yan, Buyi, Saleh, Navid B. and Wang, Peng (2018) Annealing temperature effects on photoelectrochemical performance of bismuth vanadate thin film photoelectrodes. RSC Advances, 8 (51). pp. 29179-29188. ISSN 2046-2069

[img]
Preview
Text (Full text)
Shi et al - Annealing temperature effects on photoelectrochemical performance of bismuth vanadate thin film photoelectrodes OA.pdf - Published Version
Available under License Creative Commons Attribution 4.0.

Download (1MB) | Preview
Official URL: http://dx.doi.org/10.1039/c8ra04887h

Abstract

The effects of annealing treatment between 400 °C and 540 °C on crystallization behavior, grain size, electrochemical (EC) and photoelectrochemical (PEC) oxygen evolution reaction (OER) performances of bismuth vanadate (BiVO4) thin films are investigated in this work. The results show that higher temperature leads to larger grain size, improved crystallinity, and better crystal orientation for the BiVO4 thin film electrodes. Under air-mass 1.5 global (AM 1.5) solar light illumination, the BiVO4 thin film prepared at a higher annealing temperature (500-540 °C) shows better PEC OER performance. Also, the OER photocurrent density increased from 0.25 mA cm-2 to 1.27 mA cm-2 and that of the oxidation of sulfite, a hole scavenger, increased from 1.39 to 2.53 mA cm-2 for the samples prepared from 400 °C to 540 °C. Open-circuit photovoltage decay (OCPVD) measurement indicates that BiVO4 samples prepared at the higher annealing temperature have less charge recombination and longer electron lifetime. However, the BiVO4 samples prepared at lower annealing temperature have better EC performance in the absence of light illumination and more electrochemically active surface sites, which are negatively related to electrochemical double-layer capacitance (Cdl). Cdl was 0.0074 mF cm-2 at 400 °C and it decreased to 0.0006 mF cm-2 at 540 °C. The OER and sulfide oxidation are carefully compared and these show that the efficiency of charge transport in the bulk (ηbulk) and on the surface (ηsurface) of the BiVO4 thin film electrode are improved with the increase in the annealing temperature. The mechanism behind the light-condition-dependent role of the annealing treatment is also discussed.

Item Type: Article
Subjects: H600 Electronic and Electrical Engineering
J500 Materials Technology not otherwise specified
Department: Faculties > Engineering and Environment > Mechanical and Construction Engineering
Depositing User: Paul Burns
Date Deposited: 01 Mar 2019 17:18
Last Modified: 01 Aug 2021 12:46
URI: http://nrl.northumbria.ac.uk/id/eprint/38269

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics