Arc Ablation Behavior and Microstructure Evolution of Plastically Deformed and Micro-alloyed Cu-Cr-Zr Alloys

Zhou, Kai, Chen, Wenge, Feng, Pei, Yan, Fanglong and Fu, Richard (2020) Arc Ablation Behavior and Microstructure Evolution of Plastically Deformed and Micro-alloyed Cu-Cr-Zr Alloys. Journal of Alloys and Compounds, 820. -153123. ISSN 0925-8388

[img] Text
manuscript11-13 Fu.pdf - Accepted Version
Restricted to Repository staff only until 23 November 2020.
Available under License Creative Commons Attribution Non-commercial No Derivatives 4.0.

Download (1MB) | Request a copy
Official URL: https://doi.org/10.1016/j.jallcom.2019.153123

Abstract

Cu–Cr–Zr alloys are often subjected to premature failures due to arc erosion at moment of their breakdown. In this paper, a series of simulated high-voltage arc ablation experiments were conducted to systematically investigate arc ablation characteristics of Cu–Cr–Zr alloys, their microstructure evolutions and anti-ablation properties after plastic deformation and microalloying. Results showed that during their arc ablation processes, a halo pattern was firstly formed on the surface under the action of high-temperature arc. This is followed by partial melting and splashing of Cu, forming of uneven and rough surfaces, and finally significant burning of the alloy. The degree of ablation of alloy is aggravated with the increased breakdown voltage. Due to a combined effect of solid solution strengthening, fine grain strengthening and deformation strengthening, the ablation resistance of the micro-alloyed and plastically deformed alloy has been significantly improved. The breakdown field strengths of commercial Cu–Cr–Zr alloy, heat-treated and deformed one, micro-alloyed and heat-treated one are 1.46 × 106 V/m, 1.67 × 106 V/m and 1.90 × 106 V/m, respectively. However, the breakdown strength of alloys after microalloying is unstable. Results show that there are no preferred phases for the first breakdown of arc ablation of Cu–Cr–Zr alloys. The second-phase particles with high-hardness and high-melting temperature hinder the splashing and flow of the molten copper, and inhibit the movement of the cathode spots during the ablation process.

Item Type: Article
Uncontrolled Keywords: Cu-Cr-Zr alloy, Arc ablation, Microstructure, Ablation mechanism
Subjects: F200 Materials Science
Department: Faculties > Engineering and Environment > Mathematics, Physics and Electrical Engineering
Depositing User: Elena Carlaw
Date Deposited: 21 Nov 2019 09:41
Last Modified: 10 Mar 2020 14:45
URI: http://nrl.northumbria.ac.uk/id/eprint/41557

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics